| PTN201 | 适用于高光、平面、哑光、砂纹、桔纹等表面，可实现150℃/15分钟固化
Suitable for high gloss, flat, matte, sand texture, wrinkle texture and other surfaces, and can achieve 150℃/15 minutes curing | 0.3-1%(预混)
pre-blending |
| PTN202 | 不易黄变、不影响流平，适用于各种体系，可实现150℃/15分钟固化
It is not easy to yellowing and does not affect leveling. It is suitable for various systems and can be cured at 150℃/15 minutes. | 0.1-0.6%(预混)
pre-blending |
| PTN203 | 适用于低光泽体系，对光泽影响小，可实现130℃/30分钟固化
Suitable for low gloss systems, with little effect on gloss, and can be cured at 130℃/30 minutes | 0.3-1%(预混)
pre-blending |
| PTN204 | 适用于高光、平面、桔纹等表面，可实现130℃/20分钟固化
Suitable for high gloss, flat, orange-striped surfaces, etc., and can be cured at 130℃/20 minutes | 0.1-0.4%(预混)
pre-blending |
| PTN205 | 降低固化温度，缩短固化时间，提升物理性能，不影响光泽流平
Reduce curing temperature, shorten curing time, improve physical properties, and do not affect gloss and leveling | 0.3-1%(预混)
pre-blending |
| PTN206 | 适用范围广，降低固化温度，缩短反应时间，可用于热转印粉末
Wide range of applications, lower curing temperature, shorten reaction time, can be used for thermal transfer powder | 0.3-1%(预混)
pre-blending |
| PTN207 | 适用于高光，消光体系，可实现低温固化，对涂膜表面和光泽影响小
Suitable for high gloss and matt systems, can achieve low temperature curing, and has little effect on the coating surface and gloss | 0.3-1%(预混)
pre-blending |
| PTN208 | 适用于纯环氧体系粉末涂料，提高反应速度，降低反应温度
Applicable to pure epoxy system powder coatings, increasing reaction speed and reducing reaction temperature | 0.1-0.3%(预混)
pre-blending |