| PTN601 | 提升粉末带电性，提升上粉率，降低法拉第效应，提升粉末利用率
Improve powder charge, increase powder loading rate, reduce Faraday effect, and improve powder utilization | 0.2-0.5%(预混)
pre-blending |
| PTN602 | 提高工件凹槽、死角上粉，提升粉末带电性
Improve workpiece grooves, dead corner powdering, and improve powder charging | 0.2-0.6%(预混)
pre-blending |
| PTN603 | 提高工件凹槽、死角上粉，提升粉末利用率，特别是复杂工件的喷涂
Improve the powder coating of workpiece grooves and dead corners, improve powder utilization, especially for spraying complex workpieces | 0.2-0.6%(预混)
pre-blending |
| PTN604 | 提高工件凹槽、死角和异型工件的上粉率，同时可用于摩擦枪，提升粉末带电性
Improve the powder loading rate of workpiece grooves, dead corners and special-shaped workpieces. It can also be used in friction guns to improve the powder charging performance. | 0.2-0.5%(预混)
pre-blending |
| PTN605 | 可以后混加入，用于提高粉末带电性，提升上粉率，提高粉末的雾化
It can be added after mixing to improve the charge of the powder, increase the powder loading rate, and improve the atomization of the powder. | 0.1-0.5% (后混)
dry-blending |
| PTN606 | 有效解决静电累积、电场不均导致的粉末局部掉粉现象，降低涂层表面电阻，抗静电性能好
Effectively solve the problem of local powder shedding caused by static electricity accumulation and uneven electric field, reduce the surface resistance of the coating, and have good antistatic performance | 0.2-0.5%(预混)
pre-blending |